Avantaj pwodwi yo
1. Materyèl & sele mekanis
FKM O-rings are molded from fluorocarbon rubber (vinylidene fluoride-hexafluoropropylene copolymer) with reinforcing fillers and curing agents. Sealing occurs via compression: contact stress exceeds medium pressure to block leakage. Failure when compression set >25%, swell >15%, oswa sifas fant.
2. Rezistans tèmik & chimik
Sèvis: -45 degre a 300 degre kontinyèl, ak pik tanzantan jiska 250-300 degre .. Konpatib ak 1600+ pwodwi chimik enkli. lwil mineral, gaz, aromat, ozòn. Anfle nan ASTM Fuel B (40 degre × 72h) Mwens pase oswa egal a 8% (ASTM D471). Pa pou ketonn, ester, amine, fuming asid nitrique, vapè sipèchofe.
3. Konpwesyon ansanm & dureté
Dite: Shore A 70±5 (koutim 60 ~ 90). Konpresyon seri (200 degre × 70h, 25% konpresyon) Mwens pase oswa egal a 30% (ASTM D395). Tensile pi gran pase oswa egal a 16MPa, elongasyon pi gran pase oswa egal a 150%.
4. sifas & dimansyon presizyon
Deflashing kriyojenik (taye mwens pase oswa egal a 0.1mm). Sifas Ra Mwens pase oswa egal a 1.6μm, pa gen bul, fant, oswa flash. Tolerans: GB/T 3452.1 M2 (± 0.080.13mm pou C/S; ID/OD tou M2).
5. Jeyometri estanda
Seksyon transvèsal-sikilè, pa gen okenn pati k ap deplase. Konfòme ak GB/T 3452.1, AS568, ISO 3601. Estanda sou -etajè a-, koutim pou chak desen.
Espesifikasyon pwodwi
| Paramèt | Spesifikasyon |
|---|---|
| Materyèl | Creole FKM (Fluorokarbone) |
| Dite (Shore A) | 70±5 |
| Tanperati sèvis | -45 degre ~ +300 degre |
| Rapò konpresyon rekòmande | Estatik axial: 15% ~ 30%; Radial estatik: 20% ~ 35%; Dinamik: 10% ~ 20% |
| Max Presyon Travay | San yo pa bag backup Mwens pase oswa egal a 10MPa; ak bag backup Pi gwo pase oswa egal a 30MPa |
| Seksyon transvèsal - (C/S) Range | 1.0 ~ 7.0mm (gwosè komen ki nan lis pi wo a) |
| ID/OD | Tout gwosè estanda GB / AS568; koutim OD Pi gran pase oswa egal a 1.8mm |
| Fòm{0}}seksyon transvèsal | O-ring (sikilè) |
| Koulè | Nwa (estanda), mawon / vèt opsyonèl |
| Estanda | GB/T 3452.1 / AS568 / ISO 3601 / desen koutim |
| Flash taye | 45 degre fann, taye presizyon Mwens pase oswa egal a 0.1mm |
| Konpresyon Set (200 degre × 70h) | Mwens pase oswa egal a 30% (ASTM D395) |
| Fòs rupture | Pi gran pase oswa egal a 16 MPa |
| Allongement nan Break | Pi gran pase oswa egal a 150% |
| Sifas sifas | Ra Mwens pase oswa egal a 1.6μm |
| Anbalaj | PE sele sak, katon make ak pakèt, dat, materyèl |
Enstalasyon & OperasyonPwosedi
Zòn sa a esplike espesifikasyon fonksyònman estanda konplè pou enstalasyon O-bag, ki kouvri pre-enspeksyon asanble, wilaj, metòd aliye, kalibrasyon pousantaj konpresyon ak wo-presyon anti-pwoteksyon ekstrizyon pou asire pèfòmans sele ak lavi sèvis.
01
Preparasyon anvan-enstalasyon
Byen netwaye sifas poze sele yo pou netwaye kontaminan yo epi enspekte pou rayi, twou oswa bav sou pati akonpayman yo.
02
Sifas lubrification
Aplike grès fliyò konpatib oswa lwil sistèm nan O-bag pou diminye koyefisyan friksyon epi evite domaj sifas pandan asanble a.
03
Standardize aliye ak chèk konpresyon
Sèvi ak ensèsyon espiral oswa manch rad pou enstale bag san trese; mezire dimansyon glann pou verifye rapò konpresyon nan seri estanda epi teste mouvman arbr lis.
04
Konfigirasyon pwoteksyon wo -presyon
Pou presyon ki pi wo a 10MPa, anfòm bag backup PTFE/PEEK sou bò presyon pou kontwole twou vid ki genyen ekstrizyon epi sispann echèk ekstrizyon O-bag.